Synthesis of functional fluorinated polyhedral oligomeric silsesquioxane (&#34;f-poss&#34;)

ABSTRACT

Each Rf represents a nonreactive, fluorinated organic group, R1 represents a first monovalent organic group comprising at least two carbon atoms, and R2 represents hydrogen or a second monovalent organic group comprising at least two carbon atoms. The F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane are then dried on the inert surface.

Pursuant to 37 C.F.R. § 1.78(a)(4), this application is a divisional of pending U.S. application Ser. No. 15/708,382 (filed Sep. 19, 2017), which was a divisional of U.S. application Ser. No. 14/990,973 (filed Jan. 8, 2016 and now U.S. Pat. No. 9,790,377), entitled SYNTHESIS OF FUNCTIONAL FLUORINATED POLYHEDRAL OLIGOMERIC SILSESQUIOXANE (“F-POSS”), which was a divisional of U.S. application Ser. No. 13/624,151 (filed Sep. 21, 2012 and now U.S. Pat. No. 9,249,313), entitled SYNTHESIS OF FUNCTIONAL FLUORINATED POLYHEDRAL OLIGOMERIC SILSESQUIOXANE (F-POSS), which claimed the benefit of and priority to prior filed Provisional Application Ser. No. 61/537,122, filed Sep. 21, 2011. This application is related to U.S. application Ser. No. 14/662,305 (AFD-1207DIV) filed Mar. 19, 2015; Ser. No. 13/624,355 (AFD-1207) filed on Sep. 21, 2012; and 61/537,125 (AFD-1207P) filed Sep. 21, 2011. The disclosures of these applications are expressly incorporated herein by reference, in their entireties.

RIGHTS OF THE GOVERNMENT

The invention described herein may be manufactured and used by or for the Government of the United States for all governmental purposes without the payment of any royalty.

FIELD OF THE INVENTION

The present invention relates generally to silsesquioxane materials and, more particularly to silsesquioxane materials having increased hydrophobicity.

BACKGROUND OF THE INVENTION

Polyhedral Oligomeric SilSesquioxanes (“POSS”) are cage-structures having a silicon-oxide (SiO_(1.5)) core surrounded by aliphatic or aromatic organic functionality. One such POSS derivative, octakis(1H,1H,2H,2H-heptadecafluorodecyl) POSS (“F-POSS”), possesses a periphery of long-chain fluorinated alkyl groups and has been determined to possess the lowest surface energy value of any crystalline solid (γ_(sv)=9.3 mN/m). Superhydrophobic (contact angles of a water droplet exceeding 150°) and oleophobic (repelled by oil) surfaces have been produced by casting F-POSS materials onto a substrate or blending the F-POSS material into a polymer matrix.

Conventionally, F-POSS has been used as standalone compounds without further reactive chemical functionality; however, this absence of reactive chemical functionality limits solubility in common solvents, the mechanical robustness, and abrasion resistance of surfaces comprising these materials. One attempt to overcome such limitations has been an incompletely-condensed F-POSS compound with silanol functionality, which enabled new, robust, low surface energy hybrid materials. In fact, incompletely-condensed silsesquioxane frameworks have emerged with alkyl and/or aryl peripheries and are operable as synthons for creating hybrid inorganic-organic materials, as models for silica, for catalyst support, and as precursors for other silsesquioxane containing polymers.

Unfortunately, none of the conventional synthesis strategies are viable to produce long-chain (more than three carbon atoms) F-POSS compounds possessing additional reactive or non-reactive functionality beyond alkyl or aryl peripheries. Exemplary strategies, such as those described in U.S. Pat. No. 7,053,167, entitled SILSESQUIOXANE DERIVATIVE HAVING FUNCTIONAL GROUP, issued to Ito et al. on Apr. 8, 2004 and U.S. Pat. No. 7,291,747, entitled NOVEL SILICON COMPOUNDS AND PROCESS FOR PREPARATION THEREOF, issued to Oikawa et al. on Nov. 6, 2007 (disclosures incorporated herein by reference, in their entireties), have not produced long-chain F-POSS-(ONa)₃ having more than three carbon atoms. Modified methods have produced (3,3,3-trifluoropropyl)₇Si₇O₉(ONa)₃, which can be derivatized with long-chain fluorinated trichlorosilanes to produce low surface energy materials, but the trifluoropropyl groups are still limited in chain length.

While these conventional methods have proven successful for the synthesis of incompletely-condensed compounds possessing alkyl- and aryl-functionality, there remains a need for a method of synthesizing an incompletely-condensed, long-chain F-POSS compound.

SUMMARY OF THE INVENTION

The present invention overcomes the foregoing problems and other shortcomings, drawbacks, and challenges of synthesizing an incompletely-condensed, long-chain F-POSS compound. While the invention will be described in connection with certain embodiments, it will be understood that the invention is not limited to these embodiments. To the contrary, this invention includes all alternatives, modifications, and equivalents as may be included within the spirit and scope of the present invention.

A method of forming a hydrophobic and oleophobic surface by spin coating an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface. The F-POSS has a structure:

Each R_(f) represents a nonreactive, fluorinated organic group, R₁ represents a first monovalent organic group comprising at least two carbon atoms, and R₂ represents hydrogen or a second monovalent organic group comprising at least two carbon atoms. The F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane are then dried on the inert surface.

Still other embodiments of the present invention include method of forming a hydrophobic and oleophobic surface by spin coating an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface. The F-POSS has a structure:

Each R_(f) represents a nonreactive, fluorinated organic group, R₁ represents a first monovalent organic group comprising at least two carbon atoms, and R₂ represents hydrogen or a second monovalent organic group comprising at least two carbon atoms. The F-POSS 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane are then dried on the inert surface.

One embodiment of the present invention is directed to a method of include method of forming a hydrophobic and oleophobic surface by spin coating an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface. The F-POSS has a structure:

Each R_(f) represents a nonreactive, fluorinated organic group, R₁ represents a first monovalent organic group comprising at least two carbon atoms, and R₂ represents hydrogen or a second monovalent organic group comprising at least two carbon atoms. The F-POSS 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane are then dried on the inert surface.

The above and other objects and advantages of the present invention shall be made apparent from the accompanying drawings and the descriptions thereof.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the present invention and, together with a general description of the invention given above, and the detailed description of the embodiments given below, serve to explain the principles of the present invention.

FIG. 1 is a schematic representation of the synthesis of one embodiment of an incompletely-condensed fluoroalkyl silsesquioxane.

FIG. 2 is a flow chart illustrating a method of synthesizing an incompletely-condensed fluoroalkyl silsesquioxane in accordance with one embodiment of the present invention.

FIGS. 3A and 3B are schematic representations of two intermediates in the synthesis of FIG. 1.

FIG. 4 is a schematic representation of a crystal structure determined for the incompletely-condensed fluoroalkyl silsesquioxane.

FIG. 5 is a schematic representation of a portion of the crystal structure of FIG. 4, showing the intermolecular hydrogen bonding.

FIG. 6 is a schematic representation of crystal packing of a plurality of incompletely-condensed fluoroalkyl silsesquioxane, illustrating the hydrogen bonds between silanols.

FIG. 7 is a schematic representation of the synthesis of one embodiment of a functionalized F-POSS compound.

DETAILED DESCRIPTION OF THE INVENTION

Turning now to the figures, and in particular to FIGS. 1 and 2, a multi-step synthetic method for converting a closed-cage F-POSS compound 10 to an incompletely-condensed silsesquioxane compound 12 (hereafter, “disilanol F-POSS” 12), ((R_(f))₈Si₈O₁₁(OH)₂) is shown and described in detail. While not necessary, but for purposes of illustration, the F-POSS compound 10 includes nonfunctional groups, R_(f), which may comprise —CH₂CH₂(CF₂)₇(CF₃); however, other moieties, may also be included. Indeed, not all R_(f) groups are required to have the same functionality.

More particularly, and as provided in the flow chart 14 of FIG. 2, a single edge of the closed-cage F-POSS compound is opened (Block 16) with trifluoromethane sulfonic acid, such as triflic acid (“TfOH”), in C₆F₆ and CF₃SO₃H at 25° C. for 75 min. to form a first, unstable intermediate, which is illustrated herein as ditriflate POSS cage 18, ((R_(f))₈Si₈O₁₁(OTf)₂), which is shown in FIG. 3A. Presence of the ditriflate POSS cage formation was confirmed, despite spectral complexity, via ²⁹Si NMR. The spectrum demonstrated an equilibrium between the open and closed-cage silsesquioxane frameworks 10, 18, with resonances at −62.6 ppm, −65.0 ppm, and −67.7 ppm and an integrated ratio of 2:2:4. While not wishing to be bound by theory, it is thought that the inability to isolate the first intermediate, ditriflate POSS 18, may be attributed to the strong electron-withdrawing effects of the fluorinated alkyl groups, R_(f).

The open, single end of the ditriflate compound 18 may then be bridged with a sulfate group 20 to a second, unstable intermediate, a bridged sulfate compound 22 (FIG. 3B), ((R_(f))₈Si₈O₁₃(SO₂)), in Block 24 over a reaction time, for example, of approximately 30 min., with an excess of NBut₄HSO₄, under nitrogen. The reaction mixture separates into two liquid layers: a first, yellow aqueous layer and a second, colorless fluorinated solvent layer containing both of the closed-cage F-POSS compound 10 (FIG. 1) and the bridged sulfate compound 22. While the bridging sulfate moiety 20 appears to stabilize the electron-withdrawing F-POSS cage framework, the bridged sulfate compound 22 cannot be isolated. Its presence is confirmed, however, as another NMR-observed intermediate with ²⁹Si resonances at −64.5 ppm, −65.7 ppm, and −67.3 ppm with an integrated ratio of 2:2:4. Although the bridged sulfate compound 22 was not isolated, its endohedral geometry was deduced from x-ray crystallography data, described in detail below.

Referring again to FIG. 2, a polar fluorinated solvent/water mixture (for, example, a 10:1 ratio of solvent to water) is added to the fluorinated solvent layer (the colorless, aqueous layer above) of the reaction mixture for a time ranging from about 6 hours to about 12 hours to convert the bridged sulfate compound 22 to the disilanol F-POSS 12 of FIG. 1 (Block 26). Because the reaction requires water to be miscible with the fluorinated solvent, the polar fluorinated solvent/water mixture is necessary to yield the desired, disilanol compound.

To isolate the disilanol F-POSS 12, ethyl acetate is added to the reaction mixture, and subsequently filtered. The filtrate is collected, concentrated, suspended again in chloroform, and filtered. The collected filtrand is dried under vacuum (about 18 hours at 50° C.) to yield the product with an overall yield of approximately 53% and a molecular weight of 4009 g/mol.

The principle side product of the conversion (Block 26) is the closed cage F-POSS compound 10. Due to subtle differences in solubility between the closed cage F-POSS 10 and the disilanol F-POSS 12, disilanol F-POSS 12 may be purified from the closed cage F-POSS 10, the latter of which may be subsequently recycled (Block 28). In accordance with one embodiment of the present invention, the closed cage F-POSS 10 may be precipitated from the reacted polar fluorinated solvent/water mixture while the disilanol F-POSS 12 is subsequently precipitated from a CHCl₃ solution.

The structure of disilanol F-POSS 12 was determined by combustion analysis and multinuclear NMR (¹H, ¹³C, ¹⁹F, and ²⁹Si). The ²⁹Si NMR spectrum displayed peaks at −59.0 ppm, −65.5 ppm, and −68.1 ppm, with an integration ratio of 2:2:4, which are attributed to the C_(2v) symmetry of silsesquioxane. The peak at −59.0 ppm is attributed to the silanol groups of the POSS framework.

The crystal structure 30 for disilanol F-POSS 12, shown in FIG. 4, was obtained by growing crystals from slow evaporation in hexafluorobenzene and using a 3-circle SMARTAPEX CCD (Kusing Bruker, Billerica, Mass.) with c-axis fixed at 54.748 and temperature of about 100 K with SMART V 5.625 program. Graphite monochromated Cu_(Kα) (λ=1.54179 Å) radiation was used for data collection, the SAINT V 6.22 program (Bruker, Corp.) was used for correcting Lorentz and polarization effects, and the SADABS program (Bruker, Corp.) was used for reflection scaling.

The structure was solved from C₆F₆ by direct methods (SHELXL-97, Bruker, Corp.) and all non-hydrogen atoms refined anisotropically using full-matrix, least squares refinement on F² and determined to be monoclinic P2(1)/c. The structure contains rigid, helical-like fluoroalkyl chains that are similar to the closed cage F-POSS 10 (FIG. 1) but are attached to the open Si—O frame-work by methylene groups. The crystal structure supports the 2:2:4 ratio of silicon atoms as determined by ²⁹Si NMR spectroscopy of silicon atoms.

The crystal packing of two disilanol F-POSS molecules (illustrated as 12 a and 12 b in FIG. 5, specifically, and in FIG. 6, generally, as crystal packing) reveals a dimeric structure with two F-POSS cages forming intermolecular hydrogen bonds 32 a, 32 b between silanol groups on of adjacent ones of the F-POSS cages 12 a, 12 b. This induces an increase in the lattice volume (approximately 12884 Å³) for disilanol F-POSS 12 as compared to the volume of the closed cage F-POSS 10, which was approximately 6340 Å³. Like the hydrogen bonding between silanols on incompletely-condensed alkyl based POSS triols and diols, a dimeric contact is established from intermolecular disilanol compounds at a distance, d, of approximately 2.798 Å. These intermolecular silanols are slightly closer than intramolecular silanols, (illustrated on FIG. 5 as O1, O2, O3, O4, O5, O6, O7, O8, O9, O10, O11, O12, and O13), which are separated by a distance of approximately 2.810 Å. As described in detail below, the intermolecular silanols are reactive to chlorosilanes.

To achieve an effective convergence on the structure, certain restrains were applied, including, for example, as the thermal behavior of the structure (SIMU and DELU commands for Si1 to F36C); ISOR was applied to fluorine atoms due to the associated disorder, intermolecular distances (C—C and C—F) were retrained using the SAME command. After a stable minimum was achieved, hydrogen atoms were added at calculated positions to the alpha and beta carbon atoms. Hydrogen atoms on O1 and O13 were added using DFIX to restrain the distances (0.84 Å) to the respective oxygen atoms.

Additional details with respect to the crystal structure may be obtained from the Cambridge Crystallographic Data Centre, available at http://www.ccdc.com.ac.uk, Deposition Number 843485, the disclosure of which is incorporated herein by reference, in its entirety.

Referring now to FIGS. 1, 2, and 6, disilanol F-POSS 12 is shown to readily react with functional dichlorosilanes (Cl₂SiR₁R₂) to add a particular or desired functionality (Block 34), which may include, for example, superhydrophobic or oleophobic properties. According to one embodiment of the present invention, the disilanol F-POSS 12 was condensed with bis(n-octyl)dichlorosilane in the presence of triethylamine to yield a functionalized F-POSS compound 36 (approximately 46% yield), shown in FIG. 7, with a loss of HCl. More particularly, bis(n-octyl)dichlorosilane and disilanol F-POSS 12, in C₆F₆, are mixed for 20 minutes and followed with the addition of triethylamine, in C₆F₆, and further mixing for about 12 hours. The solution is filtered and poured into ethyl acetate, causing white solid precipitate formation. Precipitate was removed via vacuum filtration, concentrated, dissolved in diethyl ether, and filtered again. The filtrate is then collected and cooled to 0° C., affording a white precipitate, which is collected and dried under vacuum to a white powder. The primary side product isolated during the reaction was, again, the closed cage F-POSS 10 (FIG. 1).

Evaluation of the structure of the functionalized F-POSS compound 36 included multinuclear NMR (¹H, ¹³C, ¹⁹F, and ²⁹Si), FT-IR, and combustion analysis. NMR spectra were obtained on 300 MHz and 400 MHz spectrometers (Bruker Corp.) using 5 mm o.d. tubes. An inverse gated 30° pulse with a 12 second delay was used to acquire the ²⁹Si NMR spectra. The NMR spectrum produced ²⁹Si resonances at −17.8 ppm, −65.4 ppm, −68.2 ppm, and −69.0 ppm, with a ratio of 1:2:4:2, of which the resonance at −17.8 ppm was attributed to dioctyl-functionalized Si atom. Large C—H stretches observed at 2974 cm⁻¹ and 2871 cm⁻¹ in the FT-IR spectrum (Perkin Elmer Spectrum BX; Waltham, Mass.) supported the presence of the hydrocarbon chains, R₁, R₂.

As described herein, incompletely-condensed disilanol F-POSS compounds may be synthesized from fully condensed F-POSS compounds via a three-step reaction process and are reactive toward dichlorosilanes to produce a functional F-POSS compound. Crystal structures demonstrate silanol groups are hydrogen bonded via intermolecular interaction, which lowers the surface energy value beyond values observed with alkyl or aryl F-POSS compounds. Accordingly, the novel, tunable structure of the functionalized F-POSS compounds described herein provides unprecedented access to fluorinated building blocks for manufacturing low surface energy materials that are mechanically robust and abrasion resistant. For example, functionalized F-POSS 36 may be cast onto a substrate or blended with copolymers to produce surfaces having robust, abrasion resistant, superhydrophobic, and oleophobic material properties.

The following examples and comparative example illustrate particular properties and advantages of some of the embodiments of the present invention. Furthermore, these are examples of reduction to practice of the present invention and confirmation that the principles described in the present invention are therefore valid but should not be construed as in any way limiting the scope of the invention.

Example 1

Seven, long-chain F-POSS compounds, each having a different functional group, were prepared in accordance with embodiments of the present invention. The F-POSS compounds included F-POSS (no additional functional group), dihydroxy silyl F-POSS (Si—(OH)₂), dioctyl silyl F-POSS (Si—((CH₂)₇CH₃)₂), dihexyl silyl F-POSS (Si—(C₆H₅)₂), vinyl methylsilyl F-POSS (Si—(CH₃)(CH═CH₂)), acrylate methylsilyl F-POSS (Si—((CH₃((CH₂)₃OC(O)CCH═CH₂)), and methylacrylate methylsilyl F-POSS (Si—(CH₃)((CH₂)₃OC(O)C(CH₃)═CH₂)). The synthesis of each compound was confirmed using combustion analysis, FT-IR, and multinuclear NMR spectroscopy.

The long-chain fluoroalkyl periphery on F-POSS results in desirable low surface energy characteristics. Interestingly, once a non-fluorinated segment was added to an edge of F-POSS, the solubility properties change dramatically. For example, the long hydrocarbon chains present in dioctyl silyl F-POSS expanded solubility from just fluorinated solvents to include non-fluorinated solvents, such as Et₂O and CHCl₃. Even small organic modifications, such as the acrylate and methacrylate moieties on acrylate methylsilyl F-POSS and methylacrylate methylsilyl F-POSS, respectively, were sufficient to expand solubility to nonfluorinated solvents, such as Et₂O. However, phenyl and vinyl groups of dihexyl silyl F-POSS and vinyl methylsilyl F-POSS, respectively, did not improve the solubility in non-fluorinated solvents, which may be attributed to the rigidity of the phenyl and vinyl groups.

Films of each of the seven F-POSS compounds were spin cast onto seven wafers (1 inch silicon) from solutions of Asahiklin-255 (3,3-dichloro-1,1,1,2,2,-penta-fluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane) (10 mg/mL) at a rate of 900 rpm for 30 seconds and in accordance with the methods described in S. S. CHHATRE et al. “Fluoroalkylated Silicon-Containing Surfaces—Estimation of Solid-Surface Energy,” ACS Appl. Mater. Interfaces. Vol. 2 (2010) 3544-3554, the disclosure of which is incorporated herein by reference, in its entirety. Dihydroxy silyl F-POSS was spin cast in a similar manner but from C₆F₆ solution at a rate of 1400 rpm. Surfaces were smoothed to less than 5 nm rms roughness to minimize any influence of surface roughness and topology as measured via atomic force microscopy using a Nanoscope IV (Digital Instruments, Inc., whole-owned subsidiary of Veeco Instruments, Inc., Plainview, N.Y.) and optical profilometry using a Wyko NT930 (Veeco Instruments, Inc.).

The influence of functionality on non-wetting behavior was determined by examining static and dynamic contact angles of water and hexadecane on each F-POSS film surface. Water and hexadecane 10 μL droplets were positioned on the prepared wafers. Dynamic contact angles were determined by placing a 3 μL drop of the probing liquid onto a test substrate of a DataPhysics OCA20 goniometer (DataPhysics Instruments GmbH, Filderstadt, Germany). An additional 2 μL of the probing liquid was added through a dispending needle at a rate of 0.2 μL/sec and then 3 μL removed at 0.2 μL/sec. Video (ranging from 20 frames to 100 frames) was captured during the addition and removal of the probing liquid such that advancement and recession of a contact line between the droplet and the test substrate, respectively, was observed and used for determining the advancing and receding contact angles, respectively. Measurements were made from a “tangent lean” fit using a droplet fitting software (DataPhysics Instruments GmbH).

The open-cage framework of compound dihydroxy silyl F-POSS did not display any adverse effect on the wetting behavior, which was attributed to the dimeric structure formed with silanols shielded from the surface of the film. A slight increase in contact angle hysteresis, θ_(rec)−θ_(adv), for dioctyl silyl F-POSS, vinyl methylsilyl F-POSS, acrylate methylsilyl F-POSS, and methylacrylate methylsilyl F-POSS was observed when wetted with water. This slight increase was not observed for surfaces comprising the same films when wetted with hexadecane, except for dioctyl silyl F-POSS. The structure of dioctyl silyl F-POSS contains long aliphatic chains that potentially favor interaction with a long-chain organic solvent, such as hexadecane.

Dihydroxy silyl F-POSS and dihexyl silyl F-POSS displayed the lowest hexadecane hysteresis values of all film surfaces and possessed sliding angles of approximately 7°. These initial measurements demonstrate that modifications of the F-POSS structure were found to be influential on wetting properties, either increasing or decreasing contact angle hysteresis.

TABLE 1 WATER HEXADECANE LONG-CHAIN F-POSS (θ_(adv), degrees) (θ_(rec), degrees) (θ_(adv), degrees) (θ_(rec), degrees) F-POSS 124.0 ± 0.5 109.6 ± 0.7 79.1 ± 0.4 65.1 ± 0.5 Dihydroxy silyl F-POSS 116.8 ± 0.4 111.0 ± 0.6 77.4 ± 0.4 74.4 ± 0.8 Dioctyl silyl F-POSS 117.9 ± 0.5  95.5 ± 0.4 69.1 ± 1.2 23.1 ± 1.2 Dihexyl silyl F-POSS 116.2 ± 0.4 110.5 ± 0.5 76.0 ± 0.8 73.2 ± 0.4 Vinyl methylsilyl F-POSS 116.2 ± 0.4 100.6 ± 0.8 78.4 ± 0.3 70.6 ± 2.3 Acrylate methylsilyl F-POSS 118.2 ± 1.0  90.6 ± 1.0 76.8 ± 0.3 67.8 ± 1.0 Methylacrylate methylsilyl F-POSS 117.0 ± 0.6  93.8 ± 1.5 78.1 ± 0.4 63.0 ± 1.2

While the present invention has been illustrated by a description of various embodiments, and while these embodiments have been described in some detail, they are not intended to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. The various features of the invention may be used alone or in any combination depending on the needs and preferences of the user. This has been a description of the present invention, along with methods of practicing the present invention as currently known. However, the invention itself should only be defined by the appended claims. 

What is claimed is:
 1. A hydrophobic and oleophobic substrate surface comprising: a substrate having a surface; and a hydrophobic and oleophobic layer on the surface of the substrate, the hydrophobic and oleophobic layer comprising an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface, the F-POSS having a structure:

where each R_(f) represents a nonreactive, fluorinated organic group, R₁ represents a first monovalent organic group comprising at least two carbon atoms, and R₂ represents hydrogen or a second monovalent organic group comprising at least two carbon atoms.
 2. The hydrophobic and oleophobic substrate surface of claim 1, wherein R_(f) represents —CH₂CH₂(CF₂)₇CF₃.
 3. The hydrophobic and oleophobic substrate surface of claim 1, wherein R₁ is selected from the group consisting of —(CH₂)₇CH₃, —(CH₂)₃OC(O)CH═CH₂, and —(CH₂)₃OC(O)C(CH₃)═CH₂.
 4. The hydrophobic and oleophobic substrate surface of claim 1, wherein the first monovalent organic group, the second monovalent organic group, or both comprises at least three carbon atoms.
 5. The hydrophobic and oleophobic substrate surface of claim 1, wherein R_(f) represents a fluorinated alkyl group.
 6. The hydrophobic and oleophobic substrate surface of claim 1, wherein each R_(f) is separately selected from the group consisting of fluorotetradecyl, fluorododecyl, fluorodecyl, fluorooctyl, fluorohexyl, and hexafluoro-i-butyl.
 7. A hydrophobic and oleophobic substrate surface comprising: a substrate having a surface; and a hydrophobic and oleophobic layer on the surface of the substrate, the hydrophobic and oleophobic layer comprising an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface, the F-POSS having a structure:

where each R_(f) represents a fluorinated alkyl group, R₁ represents a first group having at least two carbon atoms, and R₂ represents hydrogen or a second group comprising at least two carbon atoms.
 8. The hydrophobic and oleophobic substrate surface of claim 7, wherein each R_(f) is separately selected from the group consisting of fluorotetradecyl, fluorododecyl, fluorodecyl, fluorooctyl, fluorohexyl, and hexafluoro-i-butyl.
 9. A hydrophobic and oleophobic substrate surface comprising: a substrate having a surface; and a hydrophobic and oleophobic layer on the surface of the substrate, the hydrophobic and oleophobic layer comprising an F-POSS with 3,3-dichloro-1,1,1,2,2,-pentafluoropropane/1,3-dichloro-1,1,2,2,3-pentafluoropropane onto an inert surface, the F-POSS having a structure:

where each R_(f) represents a fluorinated alkyl group, R₁ represents a first group having at least two carbon atoms, and R₂ represents hydrogen or a second group comprising at least two carbon atoms.
 10. The method of claim 9, wherein each R_(f) is separately selected from the group consisting of fluorotetradecyl, fluorododecyl, fluorodecyl, fluorooctyl, fluorohexyl, and hexafluoro-i-butyl. 